Blue High Fire Retardant Rigid Foam Blend Polyols for Vpipe-2A and LNG Infrastructure

Product Categories

Blend Polyols [105]
Grouting Materials [10]
Polyurethane Waterproof Coating [10]
Universal Seat Slider [1]
Poly Polyol & Polymer Polyol [26]
Polymeric MDI [41]
Toluene Diisocyanate TDI [10]
Polyurethane Silicone [13]
Polyurethane Catalyst [45]
Color Paste [19]
Dichloromethane [1]
Polyurethane Spray And Grouting Machine [20]
Dipropylene Glycol [2]
Propylene Glycol [1]
Pharmaceutical Intermediate [2]
Manganese Dioxide [19]
Lift And Elevator [1]

Vida New Material Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Blue High Fire Retardant Rigid Foam Blend Polyols for Vpipe-2A and LNG Infrastructure

Model NO. : Vpipe-2A

Trademark : VICUSVIDA

Origin : China

HS Code : 3907299090

Supply Ability : 10000 Tons/Year

CAS No. : 9003-11-6

Formula : C5h10o2

EINECS : 618-355-0

Molecular Principal Chain : Carbon Chain Polymer

Color : Blue

Transport Package : 200kg/Drum

Customization : Available | Customized Request

Place of Origin : China

MOQ : 1000 kg

Price : Negotiable

Delivery Time : Peak Season Lead Time: within 15 workdays, Off Season Lead Time: within 15 workdays

Payment Terms : T/T, L/C

Contact Now

Product Introduction
Vpipe-2A is a kind of high fire retardant rigid foam blend polyols by 141b base, reacting with MDI to be rigid foam,which is even foam cell, low thermal insulation,high fire retardant,no shrinkage in low temperature,
widely used in stream heat pipe,LNG, and other low temperature insulation project and so on.

Physical Property

Appearance		Light yellow transparent viscous liquid
Hydroxyl value	mgKOH/g	150-250
Dynamic viscosity (25ºC)	mPa.S	150-300
Density (20ºC)	g/ml	1.20- 1.30
Storage temperature	ºC	10-25
Storage stability	Month	6

Recommended Ratio

Raw Material	Pbw
Vpipe-2A blend polyols Isocyanate	100 100

Technology and Reactivity

Items		Manual mixing
Material temperature	ºC	20
Moulding temperature	ºC	25
cream time	s	20-30
Gel time	s	145- 185
Demold time	min	15
Free Density	kg/m3	23-24

Foam Performances

Foam density by moulding
Closed cell rate
Thermal conductivity(15ºC)
Compressive Strength
(perpendicular to the direction of rising) Dimensional Stability
(24h,-20 ºC)
(24h, 100 ºC)

ASTM D1622
ASTM D1940
ASTM C518
ASTM D 1621
ASTM D2126
ASTM D2126

30-35kg/m3
≥90%
≤22mW/(m.K)
150- 180kPa
≤1.0%
≤1.5%

Blue High Fire Retardant Rigid Foam Blend Polyols for Vpipe-2A and LNG Infrastructure

Blue High Fire Retardant Rigid Foam Blend Polyols for Vpipe-2A and LNG Infrastructure Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Vida New Material Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!